六盘水球墨铸铁管历史知识(一)

发布时间:2020-06-01 14:10 | 编辑:山西悦瀚铸管 | 0 次浏览
球墨铸铁管历史知识

球墨铸铁管历史知识(一)


  球墨铸铁是20世纪五十年展起来的一种高强度铸铁材料,其综合性能接近于钢,正是基于其优异的性能,已成功地用于铸造一些受力复杂,强度、韧性、耐磨性要求较高的零件。球墨铸铁已迅速发展为仅次于灰铸铁的、应用十分广泛的铸铁材料。所谓“以铁代钢”,主要指球墨铸铁。

 

  球墨铸铁是通过球化和孕育处理得到球状石墨,有效地提高了铸铁的机械性能,特球墨管别是提高了塑性和韧性,从而得到比碳钢还高的强度。

 

  法国的雷奥姆尔(Reaumur)于1722年制成了白心可锻铸铁。后来,美国的塞斯·包伊登(Seth·Boyden)于1826年发明了黑心可锻铸铁。


雷奥姆尔.jpg

雷奥姆尔



History knowledge of ductile iron pipe (1)


Nodular cast iron is a kind of high strength cast iron material developed in the 1950s. Its comprehensive properties are close to that of steel. It is based on its excellent properties that nodular cast iron has been successfully used to cast some parts with complex stress, high strength, toughness and wear resistance requirements. Nodular cast iron has developed rapidly into a widely used cast iron material next to grey cast iron. The so-called "replacing steel with iron" mainly refers to ductile iron.

Spheroidal graphite is obtained by spheroidizing and inoculation treatment, which effectively improves the mechanical properties of the cast iron. The special spheroidal graphite pipe improves the plasticity and toughness, thus obtaining higher strength than the carbon steel.

Reaumur of France made white heart malleable iron in 1722. Later, Seth Boyden of the United States invented blackheart malleable iron in 1826.



球墨鋳鉄管の歴史知識(一)


球墨鋳鉄は20世紀50年に展开された高強度の鋳鉄材料で、その総合性能は鋼に近く、その優れた性能に基づいて、いくつかの受力複雑、強度、靭性、耐摩耗性が要求される高い部品の鋳造に成功しました。球状インキ鋳鉄は、灰鋳鉄に次ぐ幅広い鋳鉄材料に急速に発展しました。いわゆる「鉄を鋼に代える」とは、主にボール墨鋳鉄を指す。

球状黒鉛は球状黒鉛を球状に処理し、鋳鉄の機械的性質を効果的に高め、特に球状インク管は塑性と靭性を高め、炭素鋼よりも高い強度を得る。

フランスのレオウムは1722年にホワイトマイン鍛造鉄を作った。その後、米国のSeth・包伊登(Seth・Boyden)は1826年に黒心鍛造鉄を発明した。