球墨铸铁管铸造方法

发布时间:2019-01-14 12:17 | 编辑:山西悦瀚铸管 | 来源:www.zgqmztg.com | 12 次浏览
球墨铸铁管铸造方法​ 初期,铁管砂型铸造时采用水平分型面,铁管的铸造位置也是处于水平状态,为形成内腔采用细而长的砂芯,铁水在管子的整个长度上同时通过多个内浇口进入型腔以减少金属对铸型和砂芯的冲刷,并可使铁管型腔在整个长度上同时为相同温度的铁水快速,均匀地充填,但在型腔中水平安置砂芯,由于砂芯自重和受铁水浮力要引起挠度和弯曲,又会使铸管在整个长度上产生渣孔,气孔的缺陷,故铁管质量较低,只能用来铺设...

球墨铸铁管铸造方法


​        初期,铁管砂型铸造时采用水平分型面,铁管的铸造位置也是处于水平状态,为形成内腔采用细而长的砂芯,铁水在管子的整个长度上同时通过多个内浇口进入型腔以减少金属对铸型和砂芯的冲刷,并可使铁管型腔在整个长度上同时为相同温度的铁水快速,均匀地充填,但在型腔中水平安置砂芯,由于砂芯自重和受铁水浮力要引起挠度和弯曲,又会使铸管在整个长度上产生渣孔,气孔的缺陷,故铁管质量较低,只能用来铺设下水道。

      接下来有出现了立式砂型铸造法,采用垂直分型的专用砂箱,铁管的铸造位置也是垂直,砂型经烘干后,处于直立的位置,内装直立的砂芯,铁水从铸型上部进入型内,苏联曾用此种工艺生产的铁管铺设需耐一定水压的上水管道。

      由于砂型铸造铁管工艺复杂,生产效率低,工作条件差,产品质量较低,所以近数十件来,铁管的砂型铸造法陆续为离心铸造法和连续铸造法所代替。



流程图.gif


高温铁炉.jpg


光谱分析仪.jpg

Casting method of ductile iron pipe


       In the early stage, the horizontal parting surface was used in the sand mold casting of the iron pipe, and the casting position of the iron pipe was also in the horizontal state. In order to form the inner cavity, a thin and long sand core was used. The molten iron entered the mold cavity through a plurality of internal gates at the same time in order to reduce the erosion of the metal to the mold and the sand core, and the cavity of the iron pipe could be made in the whole length. At the same time, the hot metal at the same temperature can be filled quickly and evenly, but when the core is placed horizontally in the cavity, the deflection and bending will be caused by the dead weight of the core and the buoyancy of the molten iron, and the slag hole and gas hole will be produced in the whole length of the casting pipe, so the iron pipe is of good quality.

The volume is low and can only be used for laying sewers.

       Then came the vertical sand mold casting method, the use of vertical parting special sand box, iron pipe casting position is also vertical, sand mold after drying After drying, in an upright position, with an upright sand core inside, molten iron enters the mold from the upper part of the mold, a process used by the Soviet Union to produce iron pipes.

       Set up a water supply pipe with a certain water pressure.

       Because the sand mold casting iron pipe technology is complex, the production efficiency is low, the working condition is bad, the product quality is low, therefore nearly dozens of pieces, iron pipe.

       Sand casting is replaced by centrifugal casting and continuous casting.


离心铸管机.jpg


インキ鋳鉄管鋳造方法


       初期、鉄管砂型鋳造時には水平分型面を採用し、鉄管の鋳造位置も水平状態で、内腔で細い砂の芯を採用するため、鉄水はパイプの全体の長さの上で同時に多くの内に口を入れて型弁に入って、金属の鋳型と砂の芯のブラシを減らして、鉄の管型の腔を全体の長さにさせることができますまた、同じ温度の鉄の水が速く、均一に充填されていますが、型腔内に水平に砂の芯を置いて、砂の芯の自重と鉄水の浮力によって肩こりと屈折を引き起こすことができて、また鋳管が全体の長さの上にかす穴を発生させることができます。

量が低く、下水道を敷くしかない。

       次に、立式砂型鋳造法が発生し、垂直分断型の専用砂箱を採用し、鉄管の鋳造位置も垂直で、砂型が乾燥している乾燥した後、直立した位置にあり、内に直立した砂の芯、鉄水は鋳型の上部から型に入り、ソビエト連邦はこの技術で生産された鉄管屋である一定の水圧に耐えられる上水管を設ける。

       砂型鋳造鉄管の工芸は複雑で、生産効率が低くて、仕事の条件が悪くて、製品の品質が比較的に低いので、ここ数十件近く、鉄管の砂型鋳造法は、離心鋳造法と連続鋳造法に代えられている。


球墨铸铁管 2019年新发货.jpg


相关文章

     球墨铸管
    联系我们
山西悦瀚球墨铸管有限公司
联系人:朱元基

电话:13835631999

          0356-6967868

地址:山西省晋城市城区白水街南、黄华街东(方程国际商业服务楼1幢16层1908号)
客户案例
快速导航: